Alloy C 276 - 2.4819

Wst. 2.4819

UNS N10276

Stock program: 1.5 – 25 mm OD / 1/16” – 1.1/2” OD

Specification: ASTM B 622/ASTM B 626/ASME SB-622/ASME SB-626 / NACE MR0175/ PED 97/23 EC

Maximum service temperature: 1038°C / 1900°F


Alloy C276 is a nickel-molybdenum-chromium super alloy with a small amount of tungsten, designed to have excellent corrosion resistance in a wide range of severe environments. These contents make this nickel alloy especially resistant to pitting and crevice corrosion in reducing environments while chromium conveys resistance to oxidizing media. The low carbon content minimizes carbide precipitation during welding to maintain corrosion resistance in as-welded structures.


Characteristics

  • High nickel and molybdenum contents providing good corrosion resistance in reducing environments
  • Resistance to localized corrosion such as pitting and stress-corrosion cracking
  • Excellent resistance to phosphoric acid at all temperatures
  • C276 exhibits a good resistance to corrosion by seawater especially under crevice conditions

Market applications:

  • Chemical processes
  • Oil and gas industry
  • Pulp and paper production
  • Very high chloride environments
  • Pollution control

Technical details

Technical composition (%) Fe Cr Ni Mo Mn Cu Si P C S V
C276 min   4.0   14.5   Bal.   15.0   -   3.0   -   -   -   -   -
  max   7.0   16.5   -   17.0   2.50   4.5   0.80   0.300   0.020   0.350   1.00
Mechanical properties C276
Tensile strenght (mpa, min)   690
Yield strength (0.2% offset mpa, min)   290
Elongation (%, min)   40
Density / weight (g / cm3 / kg)   8.88